PL2744766 (T3)

Calciumsulfoaluminate cement or clinker comprising ternesite

(22) 16.07.2012

(43) 29.09.2017

(57) Summary of the corresponding patent EP2559674 (A1): Producing a hydraulically reactive clinker, comprises sintering a raw meal comprising calcium oxide, aluminum oxide-ferric oxide system, silicon dioxide and sulfur trioxide, converting the raw meal into a clinker intermediate at greater than 1200-1350[deg] C during a period of sintering, converting the clinker intermediate product at 1200-750[deg] C during the period of blasting to obtain the desired amount of (I), and a certain amount of aluminate- and ferrate phase and residues of the crystalline hightemperature phases of the raw materials with (II), (III) and (I), and cooling the clinker. Producing a hydraulically reactive clinker, comprises: sintering a raw meal comprising calcium oxide, aluminum oxide-ferric oxide system, silicon dioxide and sulfur trioxide; converting the raw meal into a clinker intermediate at a temperature of greater than 1200-1350[deg] C during a period of sintering; converting the clinker intermediate product at 1200-750[deg] C during the period of blasting to obtain the desired amount of calcium oxide silicate mineral of formula (C1 5S1 2Y) (I), and a certain amount of aluminate- and ferrate phase and residues of the crystalline high-temperature phases of the raw materials with calcium oxide of formula (C1Y) (II), tetracalcium aluminate ferrite of formula (C1 4(A1 xF1 - x)Y) (III) and (I); and cooling the clinker with the major components comprising (in wt.%) tetracalcium aluminate ferrite of formula (C1 4(A1 xF1 1- x) 3Y) (IV) (5-70), alpha dicalcium silicate or beta dicalcium silicate (1-80), (I) (5-75) and secondary phases (0-30). H1 : H 2O; C1 : CaO; A1 : Al 2O 3; F1 : Fe 2O 3; M : MgO; S1 : SiO 2; Y : SO 3; and x : not defined. Independent claims are also included for: (1) cement obtained by grinding the above mentioned clinker; and (2) a binding agent comprising the cement as the hydraulically reactive components.

(71) HeidelbergCement AG (DE)

x

Related articles:

Issue 2017-3 WO 2016/206785 A1

Mineralizer for calcium sulfoaluminate ternesite cements

(22) 16.06.2016 (43) 29.12.2016 (57) The present invention relates to a method for the production calcium sulfoaluminate (belite, ferrite) ternesite clinker using fluxes/mineralizers comprising the...

more
Issue 2022-2 WO 2022/006230 A1

Methods and systems for forming vaterite from calcined limestone using electric kiln

(22) 30.06.2021 (43) 06.01.2022 (57) Provided herein are zero carbon dioxide (CO2) emission processes and systems to carry out the processes, comprising a) calcining limestone in a cement plant in an...

more
Issue 2015-12 US 2015/0299040 A1

Molten salt synthesis for manufacture of cement precursors

(22) 08.11.2013 (43) 22.10.2015 (57) A method of manufacturing calcium silicates, calcium aluminates, calcium aluminosilicates and calcium ferrites and the products thereby derived utilizing...

more
Issue 2020-10 KR20200076340 (A)

Low carbon low burning cement clinker and preparing method thereof

(22) 19.12.2018 (43) 29.06.2020 (57) The present invention is a low-temperature calcined cement clinker comprising Iimit and calcium silicate, the cement clincher is a low-grade limestone having a CaO...

more
Issue 2017-4 WO 2017/017376 A1

Long-workability calcium aluminate cement with hardening ­promoted by a temperature increase, and related use

(22) 27.07.2016 (43) 02.02.2017 (57) The invention relates to a calcium aluminate cement containing a calcium aluminate with a first crystallized mineralogical phase of calcium dialuminate CA2,...

more