SG11201900700S (A)

Fly ash, cement composition, and production method for fly ash

(22) 19.09.2017

(43) 27.02.2019

(57) Fly ash, cement composition, and production method for fly ash: Provided are fly ash, a cement composition containing the fly ash, and a method for preparing fly ash, the fly ash being capable of suppressing deterioration in fluidity to improve workability and suppressing color unevenness. In the fly ash, a content of particles having a particle diameter of 45 μm or more measured by a Laser diffraction particle size analysis method is lower than 38 vol%, and a content of particles having a particle diameter of less than 5 μm measured by the analysis method is 12 vol% or lower. In addition, the cement composition comprises the fly ash and cement.

(71) Sumitomo Osaka Cement Co., Ltd (JP)

Related articles:

Issue 2019-7-8 AU2017411816 (A1)

Cement composition, method for producing same, and method for producing fly ash for cement composition

(22) 19.09.2017 (43) 18.04.2019 (57) Provided are: a cement composition that retains properties as a mixing material such as improving fluidity and contributing to a strength development, said cement...

more
Issue 2018-1-2 US 2017/0275203 A1

Cement composition and manufacturing method for cement cured body using same

(22) 25.08.2015 (43) 28.09.2017 (57) Provided is a cement composition that has high fluidity (for example, a 0-drop flow value of 200 mm or more) before curing and exhibits high compressive strength...

more
Issue 2019-6 SG10201901401R (A)

Cement composition and manufacturing method for cement cured body using same

(22) 25.08.2015 (43) 28.03.2019 (57) Provided is a cement composition that has high fluidity (for example, a -drop flow value of 200 mm or more) before curing and exhibits high compressive strength...

more
Issue 2019-12 WO 2019/165275 A1

Cement chemistries

(22) 22.02.2019 (43) 29.08.2019 (57) A method of curing a low Ca/Mg cement composition is described that includes providing a predetermined quantity of the low Ca/Mg cement composition in uncured...

more
Issue 2016-5 EP 2 838 574 B1

Admixture and method for freeze-thaw damage resistance and scaling damage resistance of cementitious compositions

(22) 19.04.2013 (43) 25.02.2015 (45) 09.03.2016 Description: Provided are a freeze-thaw damage resistance and scaling damage resistance admixture and a method of preparing a freeze-thaw damage...