US 2015/0299040 A1

Molten salt synthesis for manufacture of cement precursors

(22) 08.11.2013

(43) 22.10.2015

(57) A method of manufacturing calcium silicates, calcium aluminates, calcium aluminosilicates and calcium ferrites and the products thereby derived utilizing molten-salt synthesis and/or molten-salt sintering. Molten-salt synthesis enables efficiently manufacture calcium silicate (Ca–SiO3), dicalcium silicate (Ca2SiO4), tricalcium disilicate (Ca3Si2O7) and related compounds such as calcium aluminate (CaAl2O4), Gehlenite (Ca2Al2–SiO7) and tetracalcium aluminoferrite (Ca4Al2Fe2OO10) at temperatures in the range of about 400-750° C. The composition of the synthesized product(s) can be varied by altering the ratio of the precursor compounds and by changing the molten-salt composition, whether used as a sintering flux or molten bath, resulting in the ability to manufacture calcium silicates and related compounds for a wide variety of uses, but most specifically as precursors to the manufacture of hydraulic cements or for use in hydraulic cements such as Portland cements and calcium aluminate and other cements.

(71) Verdant Cement LLC, Wilmette, IL (US)

Related articles:

Issue 2017-11 PL2744766 (T3)

Calciumsulfoaluminate cement or clinker comprising ternesite

(22) 16.07.2012 (43) 29.09.2017 (57) Summary of the corresponding patent EP2559674 (A1): Producing a hydraulically reactive clinker, comprises sintering a raw meal comprising calcium oxide, aluminum...

more
Issue 2017-4 WO 2017/017376 A1

Long-workability calcium aluminate cement with hardening ­promoted by a temperature increase, and related use

(22) 27.07.2016 (43) 02.02.2017 (57) The invention relates to a calcium aluminate cement containing a calcium aluminate with a first crystallized mineralogical phase of calcium dialuminate CA2,...

more
Issue 2017-5 US 2017/0073239 A1

Shape-controlled cement hydrate synthesis and self-assembly

(22) 06.05.2015 (43) 16.03.2017 (57) In some embodiments, the present disclosure pertains to methods of forming calcium-silicate-hydrate particles by mixing a calcium source with a silicate source. In...

more
Issue 2019-5 EP 3 447 036 A1

Cements and cement mixtures having high mechanical properties at young ages

(22) 19.04.2016 (43) 27.02.2019 (57) Portland cements of type and category CEM I 52.5 R are described according to standard UNE-EN 197-1 and which additionally have a granulometric distribution with a...

more
Issue 2019-1-2 HRP20181382 (T1)

Ultra-fast setting cement based on amorphous calcium aluminate

(22) 28.08.2018 (43) 19.10.2018 (57) Summary of the corresponding patent WO2015173525 (A1): The invention relates to an ultra-fast setting cement composition comprising at least amorphous calcium...

more