Stabilized aqueous suspension for initiating setting and hardening of aluminous cement compositions

(22) 19.10.2016

(43) 11.10.2018

(57) A long-term stabilized aqueous initiator composition, which includes components for curing of a two-component mortar system composition. The long-term stabilized aqueous ini-tiator composition includes an activator component that has an alkali and/or alkaline earth metal salt, an accelerator component that has a water-soluble alkali and/or alkaline earth metal salt, a retarder selected from citric acid, tartaric acid, lactic acid, salicylic, gluconic acid, and a mixture of these components, a mineral filler selected from a limestone filler, corundum, dolomite, alkaline-resistant glass, crushed stone, gravel, pebble, and a mixture of these components, a thickening agent, and water.

(71) Hilti Aktiengesellschaft, Schaan (LI)

(73) Hilti Aktiengesellschaft, Schaan (LI)

Related articles:

Issue 1-2/2019 US 2018/0298268 A1

Cement having cross-linked polymers

(22) 26.06.2018 (43) 18.10.2018 (57) A composition and method of forming a wellbore cement that includes a cross-linked polyamide. The polyamide is formed by reacting a di-functional amine with an...

more
Issue 3/2016 US 2016/0024307 A1

Use of polycarboxylate ethers in combination with other additives for milling cement

(22) 06.03.2014 (43) 28.01.2016 (57) Use of an aqueous composition containing at least one poly­carboxylate ether as cement grinding aid, wherein the aque­ous composition contains one or more...

more
Issue 12/2018 WO2018185072 (A1)

Use of fine calcium carbonate in an inorganic mortar system based on aluminous cement to increase load values

(22) 03.04.2018 (43) 11.10.2018 (57) The present invention pertains to a use of calcium carbonate having an average particle size in the range of from 0.5 to 3 ?m, preferably of from 1 to 3 ?m, in an...

more
Issue 11/2018 US 2018/0230057 A1

White cementitious compositions

(22) 11.04.2018 (43) 16.08.2018 (57) A cementitious composition includes (i) white Portland cement having a fineness of about 350-550 m2/kg, D90 between about 11-50 ?m, and total combined iron oxide,...

more
Issue 6/2018 WO2018062583 (A1)

Polymer compound for admixture of cement composition

(22) 28.09.2016 (43) 05.04.2018 (57) Disclosed is a polycarboxylic acid-based copolymer compound formed as a result of the copolymerization of a polyalkylene glycol monoalkenyl ether monomer and an...

more