Progress of hydration and the structural development of hemihydrate plaster

Summary: The phase composition of a hemihydrate binder is crucial for its technological properties such as water demand, workability and rate of hydration. This work deals with the influence of different phase compositions in the binder on the hydration and the resulting solid body properties. This complex process can be reduced to a few characteristic parameters by approximation of this structure formation in a functional relationship.

1 Hydration and hardening of gypsum-based plasters

The hardening of gypsum building materials is based on the crystallization of calcium sulfate dihydrate from a solution that is supersaturated with respect to this phase. The intergrowth and interlocking of the resulting dihydrate crystals is mainly responsible for the formation of a solid body structure and is therefore the source of the strength and stability of gypsum products.

 

Calcium sulfate occurs in nature as dihydrate, known as gypsum rock, or as water-free anhydrite II. Both phases are used as natural raw materials for the building...

Related articles:

Issue 5/2015 UNIVERSITY OF SIEGEN

Investigations of the hydration of calcium sulfate hemihydrate

1 Introduction Gypsum is one of the most used materials in the world; 119 million tons of natural gypsum were extracted worldwide in 2006 (MINERAL COMMODITY 2007). Additionally another...

more
Issue 03/2009 Materials Science

Can mixtures of a- and b-hemihydrates be quantified by means of thermoanalysis?

1 Introduction Calcium sulphate-hemihydrate (CaSO4?????0.5 H2O) is manufactured from gypsum (CaSO4?????2 H2O) by partial dewatering in two different ways. In the presence of high partial water vapour...

more
Issue 5/2017 WO 2017/045519 A1

Method for producing wet-process phosphoric acid and ­byproducing alpha-hemihydrate gypsum and high-purity and high-whiteness alpha-hemihydrate gypsum

(22) 26.08.2016 (43) 23.03.2017 (57) Provided is a method for producing wet-process phosphoric acid and by-producing alpha-hemihydrate gypsum and high-purity and high-whiteness alpha-hemihydrate...

more
Issue 03/2009 Materials Science

Acceleration of the setting of hemihydrate plaster with calcium sulfate dihydrate

1 Introduction Calcium sulfate binders are required to have widely varying properties to meet technical and economic requirements. In particular, it has to be possible to vary the workability time and...

more
Issue 12/2009

Influence of calcium sulfate and calcium hydroxide on the hydration of calcium sulfoaluminate clinker

1 Introduction The production of Portland cement clinker counts for about 5??% of the total man-made CO2-emissions. A promising low-CO2 alternative is the production of alternative clinkers based on...

more