Method and system for producing low-alkalinity sulphoaluminate cement with new mineral system using steel slag

(22) 28.02.2020

(43) 06.05.2021

(57) A method and system for producing low-alkalinity sulphoaluminate cement with a new mineral system using steel slag. The method includes the following steps: evenly mixing and homogenizing ground steel slag with dry desulfurization gypsum, aluminum ash and carbide slag according to a set ratio; and conveying the homogenized raw meal to a rotary kiln for calcination to obtain cement clinker, where the calcination temperature is 1200° C-1270° C, and the calcination time is 20-60 min; the alkalinity modulus of the homogenized cement raw meal is 0.81-0.9, and the Fe₂O₃ content is 8-13%. The method breaks through the requirements on contents of calcium, aluminum and iron in traditional sulphoaluminate cement production, and realizes application of a large amount of steel slag.

(71) Shandong University, Jinan, Shandong (CN)