US 2019/0135690 A1

Process for producing a cement clinker at low temperature

(22) 07.06.2017

(43) 09.05.2019

(57) The invention provides a process for producing a cement clinker comprising: (i) mixing one or more starting materials providing each at least one or more of CaO, SiO2, AI2O3, and Fe2O3; and, optionally, SO3, to form a raw meal comprising CaO, SiO2, Al2O3, and Fe2O3; and, optionally, SO3, wherein the molar ratios among the aforementioned oxides is given by Formula I: S(CaO),(SiO2),(Al2O3), (Fe2O3),(SO3), wherein: „a“ is comprised from 0.05 to 1, „b“ is comprised from 0.1 to 0.6, „c“ is comprised from 0.001 to 0.25, and „d“ is comprised from 0 to 0.3 and wherein at least 35 % (p/p) of the starting materials of the raw meal have a critical microwaves absorbance temperature (Tc) comprised from 15 to 650° C. and a critical microwaves absorbance time (tc) comprised from 1 min to 1 h; (ii) heating the raw meal by irradiating with microwaves during 15 min to 3 h to reach a sintering temperature comprised from 300 to 950° C.; (iii) maintaining the microwave sintering temperature of step (ii) during 1 min to 3 h by further irradiating with microwaves; and (iv) cooling the clinker obtained in step (iii).

(71) Fundacion Tecnalia Research & Innovation, Derio (ES)

Related articles:

Issue 1-2/2018 EP 3 255 021 A1

Process for producing a cement clinker at low temperature

(22) 08.06.2016 (43) 13.12.2017 (57) The invention provides a process for producing a cement clinker comprising: (i) mixing one or more starting materials providing each at least one or more of CaO,...

more
Issue 9/2017 AU2015353079 (A1)

Clinker substitute material made of ­aluminium silicate and dolomite

(22) 17.11.2015 (43) 08.06.2017 (57) The invention relates to a method for producing a clinker substitute material comprising the steps: providing a starting material containing dolomite and aluminium...

more
Issue 7-8/2016 WO 2016/082936 A1

Clinker substitute material made of aluminium silicate and dolomite

(22) 17.11.2015 (43) 02.06.2016 (57) The invention relates to a method for producing a clinker substitute material comprising the steps: providing a starting material containing dolomite and aluminium...

more
Issue 12/2017 EP3224219 (A1)

Clinker substitute material made of aluminium silicate and dolomite

(22) 17.11.2015 (43) 04.10.2017 (57) Summary of the corresponding patent WO2016082936 (A1): The invention relates to a method for producing a clinker substitute material comprising the steps:...

more
Issue 1-2/2016 WO 2015/179892 A1

Apparatus for producing cement clinker

(22) 27.05.2015 (43) 03.12.2015 (57) Apparatus for producing cement clinker, comprising a kiln (3) for calcining raw materials to form cement clinker, comprising a preheating stage (2) for preheating...

more