KAZAN STATE UNIVERSITY OF ARCHITECTURE AND ENGINEERING

Structure and formation properties of a water-resistant compound binder based on calcium sulfate β-hemihydrate

This article discusses some special aspects of the hydration and structural formation of water-resistant gypsum-cement-pozzolan composite binders based on calcium sulfate β-hemihydrate modified by a group of mineral and chemical admixtures. The pore structure factors of the products based on these binders were measured and the phase compositions of the new hydration growths were studied.

1 Introduction

The main problem when mixing gypsum binder (GB) and Portland cement (PC) lies in enabling a stable structure to form during their co-hardening. Another important aspect is the problem of obtaining the required water resistance value without an appreciable increase in PC content in the mix or its dilution by means of excessive addition of active mineral admixture (AMA). It is impossible to produce competitive and durable materials based on these binders without solving these major problems.

A large body of research in this field [1-6] carried out by Volzhenskij A.V., Fischer...

Related articles:

Issue 2015-7-8 WO?2015/062749?A1

Water-resistant binder based on beta-calcium sulphate hemihydrate

(22) 03.07.2014 (43) 07.05.2015 (57) The invention relates to a binder composition comprising (a) beta-­calcium sulphate hemihydrates (b-­CaSO4???0.5?H2O), (b) Portland cement and (c) zeolite, and...

more
Issue 2015-7-8 EP 2 876 094 A1

Cement and calcium sulphate based binder composition

(22) 03.04.2014 (43) 27.05.2015 (57) The invention concerns a composition containing a) 2 to 80 weight % of Ordinary Portland Cement with respect to the total weight of the composition b) 2 to 80...

more
Issue 2017-5 AU 2017201329 A1

Method of treating industrial water

(22) 27.02.2017 (43) 16.03.2017 (57) The invention relates to a method and apparatus of removing sulphate and soluble metals such as calcium from water. The invention relates also to a method of...

more
Issue 2018-11 KAZAN STATE UNIVERSITY OF ARCHITECTURE AND ENGINEERING

Set-retarding plasticizers for improving the effectiveness of gypsum-cement-pozzolan binders

1 Introduction Materials and products based on gypsum-cement-pozzolan binders (GCPB) have not become widely used in the construction industry at present because it is necessary to use expensive input...

more
Issue 2016-9 WO 2016/115398 A1

Controlled process for precipitating calcium carbonate and vaterite precipitated calcium carbonate compositions formed by said process

(22) 14.01.2016 (43) 21.07.2016 (57) A process for converting gypsum into precipitated calcium carbonate including reacting a mixture comprising gypsum and a seed, a mineral acid, or both with at...

more