Circular economy and CO2 savings: BAM project for recycling steelmaking slag promises double benefit

Large quantities of crude iron can be recovered during steel production and at the same time a CO2-saving binder can be produced for the cement industry. The Bundesanstalt für Materialforschung und -prüfung (BAM) is currently optimising the process to bring it quickly into use.

Steel production in Germany produces over 5 million t of slag every year - a valuable resource containing about 30% iron oxide. Most of the steelmaking slag is used in asphalt and concrete for road construction, in hydraulic engineering for canals or ballast for railroad beds. This implies that the bound iron is not used according to its material potential and is lost for recycling.

A project now starting at the Bundesanstalt für Materialforschung und -prüfung (BAM) aims at a zero-waste concept, i.e. recycling the slag as completely as possible. “We want to reduce the iron oxide from the slag to metallic iron and return it to steel production,” explains Christian Adam, head of the project and an expert in circular economy at BAM. “This way, 600000 t of crude iron could be recovered every year in Germany alone, replacing 900000 t of iron ore that would otherwise have to be imported.”

BAM has already been able to demonstrate that the process works from a technical point of view. Furthermore, the process even has a second major benefit: During the iron reduction process, a high-quality mineral binder is produced as a by-product. This binder could be used in the cement industry instead of conventional Portland cement clinker. Portland cement clinker is produced from primary raw materials that have to be mined and processed with a high energy input and corresponding CO2 emissions. The cement industry is one of the world’s largest emitters of this greenhouse gas, accounting for eight percent of total CO2 emissions. The new binder could therefore help to save many tonnes of harmful greenhouse gas and at the same time reduce the raw material demand of cement production.

The technical challenge: The process requires temperatures of over 1800 °C. Up to now, however, slag in steelworks is tapped at only 1600 °C. It would therefore require a lot of energy to reach the higher operating temperature. Therefore, the process with the double benefit is neither technically feasible nor economical on an industrial scale today.

“We want to adapt the process in such a way that it can be realised on a large scale – and is profitable”, explains Christian Adam. “We will modify the composition of the slag in a way that iron recovery can be carried out at lower temperatures and thereby significantly reduce the effort of the process. At the same time, the positive properties of the reduced slag, which later give the cement strength, should be retained.”

Practical relevance and marketability are crucial here: ArcelorMittal Eisenhüttenstadt, a steel manufacturer, and two cement manufacturers, Cemex Deutschland AG and Spenner GmbH & Co. KG, participate in the project. The consortium also includes Technical University Berlin, German Aerospace Center (DLR), FEhS – Institut für Baustoff-Forschung, Öko-Institut e.V., thyssenkrupp Industrial Solutions, and LTB Lasertechnik Berlin.

Based on the project results, ArcelorMittal Eisenhüttenstadt will plan a large-scale demonstrator with which the process can be tested and integrated in a steel mill. The cement manufacturers will evaluate the performance of the binder; finally, Öko-Institut e.V. will evaluate in a life cycle assessment the ecological advantages resulting from the application of the process for both the steel and the cement industry.


See the direct link to the project:
BAM- Projekte - SlagCEM - Hochwertige Zemente und Roheisen aus Stahlwerksschlacken


Related articles:

Issue 09/2013

Metal recovery and conversion of steel slag into highly reactive cement components


1 Introduction Blastfurnace slag is the result of pig iron production and is mainly turned into granulated slag. Finely ground it shows latent hydraulic properties and is already used as a cement...


The steel production transformation process in Europe: New slag types will substitute granulated blast furnace slag

1 Background The “Green deal” strategy of the European Commission from 2019 aims to reduce the net CO2 emissions to zero by 2050. In order to reach this task breakthrough technologies have to be...


Demand for iron slag to remain high in 2020 

Demand for iron mill slag in Germany was again high last year. Due to the pandemic and the resulting decline in crude steel production to 35.7 million t, only 10.9 million t of iron slag were produced...

Issue 10/2018 US 2018/0170805 A1

Steel product, cement manufacturing process and cement

(22) 20.12.2017 (43) 21.06.2018 (57) The present invention relates to a novel cementitious product produced from steelworks slag additivation to obtain material having properties suitable for use in...

Issue 11/2009

Slags from iron and steel plants and their use in the building materials industry

The authors of the paper “Characterization of the microstructure and mineral phases of slags from German iron and steel plants” [1] investigated the mineral composition of metallurgical slags and...