Progress in building materials analyses

Within the framework of the “Major Research Instrumentation Programme“ an ultra-high resolution Nova NanoSEM 230 (field-emission low-vacuum scanning electron microscope) from the FEI Company was installed at the F. A. Finger Institute for Building Materials Science of the Bauhaus-University Weimar in October 2008 (Fig.). It consists of various components and should be seen in the context of the already existing instrumentation of the laboratory for electron microscopy. By combining the ESEM technology with the so-called Helix technology the NanoSEM 230 allows an ultra-high resolution in a gas atmosphere at low acceleration voltage (1.8 nm @ 3kV in a water vapour atmosphere). In addition to ultra-high resolution in high and low vacuum, an analytical tool installed in the NanoSEM allows the simultaneous recording of chemical (EDX) and crystallographic information (EBSD). Furthermore, cryo-prepared samples can be transferred via a docking-station to the NanoSEM equipped with a cold stage and thus investigations in deep-frozen condition become possible. The vitrification by means of high-pressure freezing, known from life science, is used to investigate nano-structural, water and/or polymer containing samples like suspensions and dispersions.


ZKG INTERNATIONAL will report in more detail on the new analysing capabilites in issue 01-2010 with a paper by Dr. Bernd Möser.

Related articles:

Issue 12/2009

Progress in building materials analyses

Within the framework of the “Major Research Instrumentation Programme“ an ultra-high resolution Nova NanoSEM 230 (field-emission low-vacuum scanning electron microscope) from the FEI Company was...

more
Issue 01/2010

Progress in building materials analysis (Part 1)

1 Introduction The properties of cementitious binders such as workability, setting behavior, strength and durability depend directly on the hydration process. In order to understand the relations...

more
Issue 02/2010

Progress in building materials analysis (Part 2)

4 Results and discussion In the following some examples are described relating to the manifold microscopic and analytical capabilities of the FEI Nova NanoSEM in combination with high-pressure...

more
Issue 10/2010

Hydration, phase and microstructure development of Ultra-High Performance Concrete

1 Introduction During the last decades Ultra-High Performance Concrete has gained more interest in research and concrete application due to the development of highly effective concrete additives. In...

more
Issue 4/2023

Effect of nano-SiO2 on the strength and hydration characteristic of low quality fly ash-cement system

1 Introduction Fly ash (FA) is a micron industrial by-product, which can cause a waste of land resources and environmental pollution when piled up in large quantities. However, its chemical...

more