PL433120 (A1)

Method of reducing the amount of cement in cementitious
compositions and the cementitious composition made according to this method

(22) 02.03.2020

(43) 06.09.2021

(57) The subject of the application is a method of reducing the amount of cement in cement mixtures, in which cement is replaced with another binder, characterized by the fact that in the binder of the cement mixture, the reduced amount of cement or cement with fly ash is replaced one to one with granite flour, using in the cement mixture as binder mixture where 70-90 wt% is cement or fly ash cement and 10-30 wt% is granite flour. The cement mixture containing binder and water, and preferably also filler and admixtures, is characterized in that the binder is a mixture of which 70-90% by weight is cement or cement with fly ash, and 10-30% by weight is granite flour.

(71) Politechnika Wrocławska (PL)

x

Related articles:

Issue 2021-3 US 2020/0407275 A1

Composition of a cement additive material as an additive to cementitious mineral admixtures, and utilized as latent hydraulic binders to improve the outcome of cementitious products

(22) 11.09.2020 (43) 31.12.2020 (57) A composition of a cement additive material to improve durability of cementitious structures, was disclosed. The cement additive composition includes an admixture...

more
Issue 2020-5-6 US 2020/0055775 A1

Early strength enhancement of cements

(22) 25.10.2017 (43) 20.02.2020 (57) A method of making a cement composition, comprising grinding a cement clinker and a strength-enhancing agent, thereby producing a hydraulic cementitious powder,...

more
Issue 2021-5 RU2748328 (C1)

Method for preparing Portland cement binder with addition of high-calcium ash from thermal power plants

(22) 14.09.2020 (43) 24.05.2021 (57) Field: building materials. Substance: invention relates to the field of building materials and can be used in the production of various concrete and mortar...

more
Issue 2022-2 WO 2021/191839 A1

Dry cementitious material mixture for 3D-printing

(22) 25.03.2021 (43) 30.09.2021 (57) A dry cementitious material mixture for 3D-printing, comprising a hydraulic cement, at least one viscosity enhancing admixture, at least one accelerator and...

more
Issue 2022-3 WO 2022/043349 A1

Limestone calcined clay cement (LC3) construction composition

(22) 25.08.2021 (43) 03.03.2022 (57) A limestone calcined clay cement construction composition comprises a) a cementitious binder comprising one or more calcium silicate mineral phases and one or more...