US 9 073 784 B2

Calcium sulfoaluminate cement with ternesite

(22) 16.07.2012

(45) 07.07.2015

(57) The present invention relates to a ternesite calcium sulfoaluminate clinker as well as a ternesite clinker containing 20 to 100 % by weight of C5S2$ and less than 15 % by weight of C4A3$, as well as the use of ternesite as an additive to calcium sulfoaluminate (ferrite) (belite) (CSA(F)(B)) clinker, calcium sulfoaluminate (ferrite) (belite) cement, and calcium sulfoaluminate (ferrite) (belite) ­binder containing 10 to 90 % by weight of CSA(F)(B) and 90 to 10 % by weight of ternesite.

(73) HeidelbergCement AG, Heidelberg (DE)

Related articles:

Issue 3/2017 WO 2016/206785 A1

Mineralizer for calcium sulfoaluminate ternesite cements

(22) 16.06.2016 (43) 29.12.2016 (57) The present invention relates to a method for the production calcium sulfoaluminate (belite, ferrite) ternesite clinker using fluxes/mineralizers comprising the...

more
Issue 09/2014 HEIDELBERGCEMENT

BCT technology receives award at the CIC

From 11.–13.06.2014, the Concrete Innovation Conference (CIC) in Oslo/Norway was the meeting place for researchers focusing on future trends in the cement and concrete industry. The event was...

more
Issue 1-2/2018 EP 3 255 367 A1

Device for manufacturing belite calcium sulfoaluminate ternesite clinker

(22) 10.06.2016 (43) 13.12.2017 (57) Device for manufacturing belite calcium sulfoaluminate ternesite clinker, comprising a rotary kiln (1) and a cooler (3), wherein a tempering device (2) is provided...

more
Issue 12/2016 EP 3 081 546 A1

Rapid-setting and hardening, high-belite sulfoaluminate cement clinker as well as application and production process thereof

(22) 09.01.2015 (43) 19.10.2016 (57) The invention discloses a rapid-hardening high-belite calcium sulfoaluminate cement clinker and relates generally to a rapid-hardening high-belite calcium...

more
Issue 9/2016 US 2016/0207834 A1

Binder comprising calcium sulfoaluminate cement and a magnesium compound

(22) 02.09.2014 (43) 21.07.2016 (57) The present invention relates to a binder comprising calcium sulfoaluminate (CSA) cement and a magnesium compound, to a method of enhancing strength development...

more