US 2022/0033304 A1

Biomass waste materials as a set-retardation agent in cement or concrete

(22) 28.07.2021

(43) 03.02.2022

(57) A concrete mixture is provided. The mixture includes cement powder, a plant biomaterial in a solid form, wherein the plant biomaterial does not comprise ash, and concrete aggregate, wherein a ratio of cement powder to the biomaterial ranges from 10:1 to 100:1. Methods of controlling concrete setting by adding a plant biomaterial in a solid form to a concrete mixture are also provided.

(71) University of Louisville Research Foundation, Inc., Louisville, KY (US)


Related articles:

Issue 2023-2 CN114591038 (A)

Cement powder and preparation method thereof

(22) 19.04.2022 (43) 07.06.2022 (57) The invention relates to the field of building materials, in particular to cement powder and a preparation method thereof. The cement powder comprises the...

Issue 2022-1 US 2021/0371334 A1

Method for producing dust-reducing and dust-absorbing material from nonmetallic mineral and raw material from cement plant

(22) 01.03.2021 (43) 02.12.2021 (57) A method for producing a dust-reducing and dust-absorbing material from a nonmetallic mineral and a raw material from a cement plant. The method includes calcining...

Issue 2022-3 US 2022/0062814 A1

System and method for mixing recirculating combustion ash with hydrated lime and water

(22) 28.08.2020 (43) 03.03.2022 (57) A mixer for recirculating ash from solid fuel combustion with hydrated lime and water and to feed the mixture into a desulfurization reactor. The mixer includes a...

Issue 2022-2 WO 2022/006230 A1

Methods and systems for forming vaterite from calcined limestone using electric kiln

(22) 30.06.2021 (43) 06.01.2022 (57) Provided herein are zero carbon dioxide (CO2) emission processes and systems to carry out the processes, comprising a) calcining limestone in a cement plant in an...

Issue 2022-5 US2022169566 (A1)

Production method for cement clinker and cement clinker powder

(22) 13.03.2020 (43) 02.06.2022 (57) Portland cement clinker that includes C3A and C4AF in total from 22 to 40 mass % calculated by Bogue’s formulas and has an iron modulus (I.M.) of 0.8 to 1.3 is...